Conductive Geopolymers as Low-Cost Electrode Materials for Microbial Fuel Cells

Abstract

Geopolymer (GP) inorganic binders have a superior acid resistance compared to conventional cement ( e.g. , Portland cement, PC) binders, have better microbial compatibility, and are suitable for introducing electrically conductive additives to improve electron and ion transfer properties. In this study, GP-graphite (GPG) composites and PC-graphite (PCG) composites with a graphite content of 1-10 vol % were prepared and characterized. The electrical conductivity percolation threshold of the GPG and PCG composites was around 7 and 8 vol %, respectively. GPG and PCG composites with a graphite content of 8 to 10 vol % were selected as anode electrodes for the electrochemical analysis in two-chamber polarized microbial fuel cells (MFCs). Graphite electrodes were used as the positive control reference material. Geobacter sulfurreducens was used as a biofilm-forming and electroactive model organism for MFC experiments. Compared to the conventional graphite anodes, the anode-respiring biofilms resulted in equal current production on GPG composite anodes, whereas the PCG composites showed a very poor performance. The largest mean value of the measured current densities of a GPG composite used as anodes in MFCs was 380.4 μA cm -2 with a standard deviation of 129.5 μA cm -2 . Overall, the best results were obtained with electrodes having a relatively low Ohmic resistance, that is, GPG composites and graphite. The very first approach employing sustainable GPs as a low-cost electrode binder material in an MFC showed promising results with the potential to greatly reduce the production costs of MFCs, which would also increase the feasibility of MFC large-scale applications.

Keywords

Identifiers

DOI

10.1021/acsomega.1c03805

PubMed

34746578

Journal

ACS Omega

Year

2021