Impact of Cold Start and Hot Stop on the Performance and Durability of a Proton Exchange Membrane (PEM) Fuel Cell
Bin Du, Richard Pollard, Manikand Ramani, Paul Graney +1
AI summary
70% confidenceRapid fuel cell performance degradation occurs after 30 cold start/hot stop cycles, primarily due to relative humidity effects on membrane/ionomer hydration.
Generated by MESSAI extraction pipeline · review against source PDF
Representative MEC — matched on the paper’s system type only, not its reactor or geometry.
Open in lab for full controls, parameter editing, and template overlays.
Open in lab →What they did
- System
- MEC
What worked
No outcome metrics extracted yet.
Abstract
Rapid fuel cell performance degradation was observed after just 30 cold start/hot stop cycles. Relative humidity (RH) was found to be the primary operating parameter associated with the rapid voltage decay during this thermal cycling. It was found that repeated thermal cycling could affect the RH inside a fuel cell and, consequently, alter the water activity of membrane/ionomer. We propose an extension of the generally accepted reverse-current carbon corrosion mechanism to account for the RH effects. The rapid voltage decay was linked to a RH- dependent cathode carbon corrosion process which was attributed to a lag in the ionomer/membrane hydration state during the thermal cycling. It has been demonstrated that one can reduce the carbon corrosion rate by avoiding the combination of cold starts and hot stops. Recommended strategies for mitigation are discussed in the context of the corrosion mechanism.
Key findings
- Repetitive thermal cycling affects relative humidity inside the fuel cell, altering water activity of membrane/ionomer.
- RH-dependent cathode carbon corrosion process causes rapid voltage decay during thermal cycling.
- Carbon corrosion rate can be reduced by avoiding cold starts and hot stops.