Effect of Gas Diffusion Layer Structure on the Performance of Hydrogen Oxygen and Hydrogen Air Polymer Electrolyte Membrane Fuel Cell

Abstract

Gas diffusion layer (GDL) plays a very important role in the function of fuel cell performance. Therefore, the requirements of an ideal GDL include diffusion and distribution of reactants to the catalyst layers, good in plane and thro plane conductivity. Depending on the reactants and operating current densities, the GDL must provide an optimum hydrophobicity and hydrophilicity for gas distribution, water and thermal management (1-3). In order to improve the stability of fuel cell stack, a complete understanding of GDL properties are essential. In the present work, AvCarb MGL370 carbon paper and AvCarb 1071 carbon cloth is used as a substrate material. The effect of PTFE content on the substrate and micro-porous layer on the fuel cell performance is compared in both hydrogen/oxygen and hydrogen/air. The properties of GDL were characterized by experimental setup developed in house for the measurement of gas diffusion coefficient. The properties were also measured using Capillary Flow Porosity meter. The percentage of PTFE on the substrate is varied for both carbon paper as well as carbon cloth ranging from 5 to 20%, however the concentration of PTFE in the micro layer is fixed. The experiments are conducted by keeping constant PTFE loading in the substrate while the concentration PTFE in the micro layer is varied from 15 to 30%. The PEMFC cells were tested at 65 °C and at ambient pressure with relative humidity of hydrogen and air kept at 90% and 80%, respectively. The results were analyzed from the polarization curves. The long-term stability of the cell is evaluated by operating the cell at constant current density. PTFE content in the substrate as well as micro porous layer is important for the performance of fuel cell. The current density achieved in the hydrogen/oxygen is about 1.25A/cm² at 0.6V, while the same electrode when operated with hydrogen air is 0.5A/cm² at the same operating voltage (GDL1). Alteration of both substrate and micro-layer PTFE concentration improve the performance to 1.6A/cm² and 0.7A/cm² at 0.6V for hydrogen/oxygen and hydrogen/air respectively (GDL2),Fig.1. The effect of hot pressing condition on both carbon cloth as well as carbon paper is also discussed. The pressing pressure conditions varied from 40 to 120kg/cm². In this paper the performance of both carbon paper and carbon cloth is discussed with respect to PTFE content and pressing conditions. Fig.1: The effect of PTFE content in the substrate and micro layer, ambient pressure, temperature of operation 65 °C, H 2 /O 2 - 100/80%, flow rate H 2 /O 2 is 300/400cc References: 1. G. Velayutham, J. Kaushik , N.Rajalakshmi , K.S.Dhathathreyan , Fuel Cell 7, 314-318 (2007) 2. G. Velayutham, International Journal of Hydrogen Energy 36(22), 14845-14850, (2011) 3. E.Passalacqua , G.Squadrito, F.Lufrano , A.Patti, L.Giorgi . J Appl Electrochem , 31, 449-54 ( 2001)

Key findings

• ▸The GDL plays a crucial role in fuel cell performance, requiring diffusion and distribution of reactants, good conductivity, and optimal hydrophobicity and hydrophilicity.
• ▸The study uses AvCarb MGL370 carbon paper and AvCarb 1071 carbon cloth as substrate materials and varies PTFE content from 5 to 20% to compare fuel cell performance.
• ▸The results show that the properties of GDL were characterized using an experimental setup and Capillary Flow Porosity meter, with implications for fuel cell stack stability.