Long‐Term Performance of Chemically and Physically Modified Activated Carbons in Air Cathodes of Microbial Fuel Cells

Abstract

Abstract Activated carbon (AC) is a low‐cost and effective catalyst for oxygen reduction in air cathodes of microbial fuel cells (MFCs), but its performance must be maintained over time. AC was modified by three methods: 1) pyrolysis with iron ethylenediaminetetraacetic acid (AC‐Fe), 2) heat treatment (AC‐heat), and 3) mixing with carbon black (AC‐CB). The maximum power densities after one month with these AC cathodes were 35 % higher with AC‐Fe (1410±50 mW m −2 ) and AC‐heat (1400±20 mW m −2 ), and 16 % higher with AC‐CB (1210±30 mW m −2 ) than for plain AC (1040±20 mW m −2 ), versus 1270±50 mW m −2 for a Pt control. After 16 months, the Pt cathodes produced only 250±10 mW m −2 . However, the AC‐heat and AC‐CB cathodes still produced 960–970 mW m −2 , whereas plain AC produced 860±60 mW m −2 . The performance of the AC cathodes was restored to >85 % of the initial maximum power densities by cleaning with a weak acid solution. Based on cost considerations among the AC materials, AC‐CB appears to be the best choice for long‐term performance.

Key findings

• ▸AC-Fe and AC-heat cathodes maintained 35% higher maximum power densities after one month compared to plain AC.
• ▸AC-CB cathodes showed 16% higher maximum power densities after one month compared to plain AC.
• ▸After 16 months, AC-heat and AC-CB cathodes still produced 960-970 mW/m², while plain AC produced 860 mW/m².

Keywords

Identifiers

DOI

10.1002/celc.201402123

Journal

ChemElectroChem

Year

2014