Self-Nitrogen-Doped Carbon Nanosheets Modification of Anodes for Improving Microbial Fuel Cells’ Performance
Xiaoye Xing, Zhongliang Liu, Wenwen Chen, Xiaoge Lou +2
AI summary
70% confidenceResearchers developed a method to create nitrogen-doped carbon nanosheets from dandelion seeds, which improved the performance of microbial fuel cells.
Generated by MESSAI extraction pipeline · review against source PDF
Representative MFC — matched on the paper’s system type only, not its reactor or geometry.
Open in lab for full controls, parameter editing, and template overlays.
Open in lab →What they did
- System
- MFC
What worked
No outcome metrics extracted yet.
Abstract
Dandelion seeds (DSs) have the advantages of high nitrogen content, low cost and easy availability and thus are ideal carbon precursors for fabricating carbon nanomaterials. Herein, this paper prepared a carbon nanosheet material by one-step carbonizing DSs with KOH activation (self-doped-nitrogen porous carbon nanosheets (N-CNS)) and without KOH activation (unactivated self-doped-nitrogen porous carbon nanosheets (N-UA-CNS)), which could dope nitrogen atoms directly into carbon materials without additional processes. Scanning electron microscopy(SEM) images and X-ray diffraction(XRD) patterns both showed that N-CNS was of macro-porous structure, and beneficial for microorganisms’ growth. The Brunauer Emmett Teller(BET) surface area of N-CNS was 2107.5 m² g⁻¹, which was much higher than that of N-UA-CNS. After carbon clothes were modified by the obtained materials, the internal resistance of both N-CNS-modified carbon cloth (N-CNS-CC) and N-UA-CNS-modified carbon cloth (N-UA-CNS-CC) was greatly reduced and was found to be only 2.7 Ω and 4.0 Ω, respectively which are all significantly smaller than that of blank carbon cloth (65.1 Ω). These electrodes were assembled in microbial fuel cells (MFCs) as anode, and the operation experiments showed that the N-CNS modification shortened start-up time, improved output stability and increased maximum output voltage significantly. The maximum power density of N-CNS-CC MFC was 1122.41 mW m⁻² which was 1.3 times of that of N-UA-CNS-CC MFC and 1.6 times of that of CC MFC. The results demonstrated that N-CNS was an ideal modification material for fabricating MFC anodes with simple preparation process and low cost.
Key findings
- N-CNS-modified carbon cloth had an internal resistance of 2.7 Ω, significantly smaller than blank carbon cloth (65.1 Ω).
- N-CNS had a higher BET surface area (2107.5 m² g⁻¹) compared to N-UA-CNS.
- Macro-porous structure of N-CNS was beneficial for microorganisms' growth.
Keywords
Identifiers
- Journal
- Catalysts
- Year
- 2020